Vicalloy Ⅰ is a cobalt-vanadium-Iron ductile permanent magnet alloy. The material is used in electrical and electrical and electronic application.magnetic properties are optimized by heat-treating cold rolled material.VicalloyⅠ has a relatively high remanence and low coercive force.
Forms: Sheet/Plate, Bar/Rod

Description

Vicalloy Ⅰ is a cobalt-vanadium-Iron ductile permanent magnet alloy. The material is used in electrical and electrical and electronic application.magnetic properties are optimized by heat-treating cold rolled material.VicalloyⅠ has a relatively high remanence and low coercive force.

Application

Vicalloy Ⅰ has been used for biasing magnets in meters and magnetic actuators, as magnetic coded devices, field coils for DC motors and servos, and hysteresis motor laminations.

parameter

Cross Reference

IEC	Russia	U.S.A	Japan
-	-	Vicalloy Ⅰ	-

Chemical Composition (%)

C	Si	P	S	Mn	Co	V	Ni	Fe
≤
0.12	0.7	0.025	0.02	≤0.7	51~53	9.5~10.5	≤0.7	Bal.

Physical Property

Density (g/cm3)	8.1
Resistivity(room temperature)/(μ•cm)	71
Thermal Coefficient (20~300℃)/( 10-6/K)	11.3
Modulus of Elasticity/MPa	186200

Magnetic Property

Magnetic field intensity(Hμ)	A/m	14400～18400
Flux Density (Bμ)	T	0.9～1.2
Pμ	erg/cm3≥	3.0×105
Kμ≥	kμ≥	0.58

Size Range

Sheet	Thickness 0.05mm~0.70mm, width:10.0~160.0mm
Plate	Thickness 3.5mm~40.0mm,width:10.0~160.0mm
Bar	Dia 8.0mm~Dia 32.0mm,length:≤2000mm
	Dia 32.0mm~Dia 150.0mm,length:≤1000mm

Condition: (With max tolerance) cold rolled,bright,hot rolled,burnished,,hot forging,peeled,turned